Q390,,,,,,, , 化学成分含量 等级,C,Mn,Si,P,S,V,Nb,Ti,Al,Cr,Ni, A,≤0.20,1.00～1.60,≤0.55,≤0.045,≤0.045,0.02～0.20,0.015～0.060,0.02～0.20,-,≤0.30,≤0.70, B,≤0.20,1.00～1.60,≤0.55,≤0.040,≤0.040,0.02～0.20,0.015～0.060,0.02～0.20,-,≤0.30,≤0.70, C,≤0.20,1.00～1.60,≤0.55,≤0.035,≤0.035,0.02～0.20,0.015～0.060,0.02～0.20,≥0.015,≤0.30,≤0.70, D,≤0.20,1.00～1.60,≤0.55,≤0.030,≤0.030,0.02～0.20,0.015～0.060,0.02～0.20,≥0.015,≤0.30,≤0.70, E,≤0.20,1.00～1.60,≤0.55,≤0.025,≤0.025,0.02～0.20,0.015～0.060,0.02～0.20,≥0.015,≤0.30,≤0.70, 力学性能 , 　　【抗拉强度】（σb/MPa）,490～650 【伸长率】（δ5/%） 等级,δ5/%, A,≥19, B,≥19, C,≥20, D,≥20, E,≥20, 【屈服点】（σs/MPa） 厚度（直径、边长）/mm,≤16,>16～35,>35～50,>50～100, σs/MPa,≥390,≥370,≥350,≥330, 【冲击吸收功】（Akv（纵向）/J） 等级￤温度,,20℃,0℃,-20℃,-40℃, A,?,?,?,?, B,≥34,?,?,?, C,?,≥34,?,?, D,?,?,≥34,?, E,?,?,?,≥27, Q390E , , 　　材料名称：低合金高强度结构钢, , 　, 　　标准：GB/T,1591-1994, , 化学成份：, , 　　碳,C：≤0.20, , 　　硅,Si：≤0.55, , 　　锰,Mn：1.00～1.60, , 　　硫,S：≤0.025, , 　　磷,P：≤0.025, , 　　铬,Cr：≤0.30, , 　　镍,Ni：≤0.70, , 　　铜,Cu：答应残余含量≤0.30, , 　　钒,V：0.02～0.20, , 　　铌,Nb：0.015～0.060, , 　　钛,Ti：0.02～0.20, , 　　钼,Mo：可少量加入, , , 　　力学性能：, , 　　抗拉强度,σb(MPa)：490～650, , 屈服强度,σs(MPa)：≤16时：≥390,,>16～35时：≥370,,>35～50时：,≥350,,>50～100时：,≥330, , 　　伸长率,δ5(%)：≥20, , 　　冲击功,Akv(J)：－40℃时：≥27, , 　　试样尺寸：试样厚度(直径,边长), , 　　交货状态：以热轧、控轧、正火及正火加回火状态交货。 单位名称：昆山奔驰特殊钢材有限公司 地址:江苏省昆山市城北国际模具城材料区7幢4号,邮编:213000 我公司：长期有大量现货供应,规格齐全,欢迎前来选购。 手机：18784552399 传真：0512-87886370 联系人：朱小姐 联系电话0512-57802609,,,57800094 QQ：358027212